Timken公司所生产的AISI/SAE 4130/4130HW无缝钢管主要应用于海工钻井平台上装配的7,500-15,000psi等级的高压泥浆管线和高压水泥管线。

一、规范性引用文件Normative Reference

ASTM A519 Standard Specification for Seamless Carbon and Alloy Steel Mechanical Tubing

ASME B36.10 Welded and Seamless Wrought Steel Pipe

ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products

ASTM E8 Standard Test Methods for Tension Testing of Metallic Materials

ASTM E18 Standard Test Methods for Rockwell Hardness of Metallic Materials

ASTM E23 Standard test methods for Notched bar impact testing of metallic materials

ASTM E112 Standard Test Methods for Determining Average Grain Size

ASTM E213 Standard Practice for Ultrasonic Examination of Metal Pipe and Tubing

NACE MR0175 Metals for Sulfide Stress Cracking and Stress Corrosion Cracking Resistance in Sour Oilfield Environments

二、钢管状态及符合的标准 Tube Condition and Standard

无缝钢管的状态为：热轧- 淬火- 回火- 去应力- 去氧化皮

钢管应符合美国ASTM  A519 《机械用无缝钢管-合金钢管的标准规范》。

三、技术要求 Technical Specification

1. 化学成分 Chemistry

2. 机械性能 Mechanical Property

抗拉强度σ_b≥655 Mpa （95ksi），屈服强度σ_s≥585 Mpa （85ksi），延伸率δ₅≥17%，断面收缩率Red≥35%，拉伸试样标距段长度为50.8 mm，圆形，取样位置为管壁中间位置。

——抗拉强度 tensile strength：s_b≥ 655 Mpa；

——屈服强度 yield strength：σ_s≥ 585 Mpa；

——伸长率（纵向）elongation (longitudinal)：d₅≥ 17%;

——断面收缩率 reduction of area：Red≥ 35%;

3. 纵向冲击功 Longitudinal Impact （可选）

平均纵向冲击功AK_V≥42 J，单个值AK_V≥30 J，夏比试验，试验温度0摄氏度，取样位置为管壁中心。

4. 硬度要求 Hardness

钢管表面洛氏硬度不超过22HRC， 符合NACE MR 01 75。

5. 钢管晶粒度 Grain Size：≥5级

6. 钢管的热处理 Heat treatment

管材需要淬火+回火状态交货。

7. 钢管的无损检测Non-destructive Inspection

钢管需要对内、外径进行探伤，以保证无有害的表面及内部缺陷。表面探伤使用Eddy（涡流）探伤方式，内径探伤使用超声波探伤方式。表面缺陷不超过壁厚的5%，内壁缺陷不超过壁厚的5%。