对 20Mn2SiCrNiMo 贝氏体/马氏体复相高强钢进行淬火-配分-回火(Q-P-T)工艺处理, 并采用紧凑 拉伸试样进行疲劳实验.
Q-P-T处理贝氏体-马氏体复相高强钢疲劳断裂特性研究FATIGUE BEHAVIOR OF BAINITE/MARTENSITE MULTIPHASE
HIGH STRENGTH STEEL TREATED BY
QUENCHING–PARTITIONING-TEMPERING PROCESS 对 20Mn2SiCrNiMo 贝氏体/马氏体复相高强钢进行淬火-配分-回火(Q-P-T)工艺处理, 并采用紧凑
拉伸试样进行疲劳实验. 结果表明, Q-P-T 工艺参数对贝氏体/马氏体复相高强钢的疲劳断裂特性具有显著
影响, 经过合理的 Q-P-T 工艺处理的贝氏体/马氏体复相高强钢具有较高的疲劳门槛值(ΔKth=13.2 MPa·m1/2)
及较低的裂纹扩展速率. 显微组织及裂纹扩展路径观察显示, Q-P-T 处理的贝氏体/马氏体复相高强钢的显
微组织包括贝氏体、马氏体和残余奥氏体薄膜, 其中“柳叶状”贝氏体及纳米级残余奥氏体薄膜可以阻碍裂
纹扩展, 迫使裂纹转折、分叉或“间断”, 这是贝氏体/马氏体复相高强钢疲劳断裂性能改善的主要因素.
Recently, low-cost advanced high strength steels (AHSS) with high toughness and fatigue limit have
been developed in order to ensure the safety and lightweight of the engineering components. As promising candidates for next generation of AHSS, the bainite/martensite multiphase high strength steels exhibit excellent
combination of strength and toughness due to the refined multiphase microstructure and retained austenite films
located between bainitic ferrite laths. The previous works showed that the mechanical properties of
bainite/martensite multiphase steels can be further improved through quenching- partitioning- tempering (Q-P-T)
process. In the present work, the effect of Q-P-T process on the microstructure and fatigue behaviors of steels was
investigated, and the relationship between the microstructure and the fatigue crack propagation was discussed in
detail. Here, a 20Mn2SiCrNiMo bainite/martensite multiphase steel was treated by Q-P-T processes: (1)
quenching to 200 ℃, partitioning at 280 ℃ for 45 min and finally tempering at 250 ℃ for 2 h (QPT200
sample); (2) quenching to 320 ℃, partitioning at 360 ℃ for 45 min and finally tempering at 250 ℃ for 2 h
(QPT320 sample). Microstructure observation showed that the QPT200 sample consisted of leaf-shaped bainite,
martensite and filmy retained austenite (RA), while some blocky martensite/austenite (M/A) islands were
observed in QPT320 sample. The volume fractions of retained austenite in QPT200 and QPT320 samples are 4.5%
and 9.8%, respectively. The fatigue crack propagation rate da/dN and threshold value of fatigue cracking ΔKth
were measured using compact-tensile specimens. The results showed that the Q-P-T process parameters had a
significant influence on the microstructures and fatigue properties of the bainite/martensite multiphase steels. The
bainite/martensite multiphase steel after appropriate Q-P-T treatment (QPT 200 sample in the present work) has
higher ΔKth and lower da/dN, which originates from the resistance on fatigue crack propagation due to the
presence of leaf-shaped bainite and nanometer-sized retained austenite films. Furthermore, although the volume
fraction of retained austenite in QPT320 sample is higher than that in QPT200 sample, the ΔKth of QPT 320
sample is lower than that of QPT200 sample. It is suggested that the effect of retained austenite on the fatigue
behaviors depends on its volume fraction, size and morphology.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.