Cu含量对含Sc铝锂合金显微组织和力学性能的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-07-05
通过显微硬度测试、常规拉伸性能测试、扫描电镜和透射电镜等观察手段研究Cu含量对含Sc铝锂合金显微组织和力学性能的影响。
Cu含量对含Sc铝锂合金显微组织和力学性能的影响Effects of Cu content on microstructure and mechanical properties of Al-Cu-Li-Sc alloy通过显微硬度测试、常规拉伸性能测试、扫描电镜和透射电镜等观察手段研究Cu含量对含Sc铝锂合金显微组织和力学性能的影响。结果表明:在Sc元素含量基本不变的情况下，Cu含量为4.2%(质量分数)的合金在均匀化过程中会形成W(AlCuSc)相，且该相在固溶时也不会完全溶解到α(Al)。在相同Sc含量条件下，随着α(Al)中Cu含量的下降，w(Cu)/w(Sc)变小，均匀化后形成的W相数量会明显降低，直至消失。由于W相对合金力学性能不利，其数量的减少可以增加合金中有效固溶Cu原子的数量，从而提高合金性能，W相的形成抑制合金中Al3(Sc,Zr)粒子的析出形成。
The effects of Cu content on the microstructure and mechanical properties of Al-Cu-Li-Sc alloys were investigated by microhardness test, tensile test, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations. The results indicate that the alloys with high Cu content will precipitate W(AlCuSc) phase during homogenization when the Sc content is same, and the W phase will not dissolve into the α(Al) at solution treatment. The amount of W phase will decrease with the reduction of Cu content while the Sc content is the same. Because of the deleterious effects of W phase on the mechanical properties, the content of Cu atoms in α(Al) improves, the precipitation of θ′ and T1 phases improve the mechanical properties after aging. The formation of Al(Sc,Zr) particles will be inhibited due to the existence of W phase.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.