采用 XRD, SEM, TEM, 硬度测试和拉伸实验研究了冷轧 Mn12Ni2MoTi(Al)钢经不同工艺退火后的显微组织及力学性能.
冷轧及退火制备的超细晶粒双相Mn12Ni2MoTi(Al)钢AN ULTRAFINE GRAINED DUPLEX Mn12Ni2MoTi(Al) STEEL FABRICATED BY COLD ROLLING AND ANNEALING采用 XRD, SEM, TEM, 硬度测试和拉伸实验研究了冷轧 Mn12Ni2MoTi(Al)钢经不同工艺退火后的显微组织及力学性能. 结果表明, 马氏体 Mn12Ni2MoTi(Al)钢经 65%冷轧及 710~745 ℃退火处理后转变成主要由奥氏体晶粒和铁素体晶粒组成的亚微米级超细晶粒双相组织, 并且弥散分布着第二相析出物颗粒; 在退火中形成的富Ti, Mo及Si的第二相颗粒阻碍了超细再结晶晶粒的粗化, 从而提高了钢的屈服强度和热稳定性; 经710 ℃, 24 h长时间退火后, 超细晶粒双相钢的平均晶粒尺寸仍然小于500 nm; 超细晶粒双相钢延伸率随室温奥氏体体积分数增加而增加, 室温奥氏体体积分数随退火温度升高或退火时间延长先增加后降低, 且在745 ℃, 0.5 h 退火时达到最大值. 超细晶粒钢的屈服强度和总延伸率可达到 900 MPa和 23%以上, 比同种材料淬火马氏体钢提高了约一倍。
For decades, transformation induced plasticity (TRIP) assisted steels with high tensile strength and exceptional ductility at room temperature have attracted a great deal of attentions. Their applications are often limited due to the low yield strength．In this work, an ultrafine grained (UFG) duplex Mn12Ni2MoTi(Al) TRIP steel with high yield strength and good ductility is fabricated by cold rolling and subsequent annealing at 710~745 ℃. The microstructure and mechanical properties of the steels with different heat treatment conditions are investigated by means of XRD, SEM, TEM, hardness and tensile test．It is found that after annealing at 710~745 ℃, the deformation microstructure of the cold-rolled samples has transformed into a sub-micron ultrafine grained (UFG) duplex microstructure consisting of austenite, ferrite and dispersed second-phase precipitations. The second-phase precipitations formed during annealing are rich in Ti, Mo and Si, and play an important role in preventing the ultrafine grains from coarsening, which results in high yield strength and good thermal stability. After annealing at 710 ℃ for 24 h, the average grain size of the UFG steel is still less than 500 nm. The elongation of the UFG duplex steel is increasing with the increment of the volume fraction of austenite in the UFG duplex steel at room temperature. The volume fraction of austenite in the UFG duplex steel at room temperature first increases and then decreases with the annealing temperature and time increasing, and reaches the maximum value when annealing at 745 ℃ for 0.5 h. The yield strength and total elongation of the UFG steel can be as large as 900 MPa and 23%, respectively, which are about double those of the quenched martensitic sample.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI
has been a reliable partner and supplier of sophisticated and high-quality
semi-finished products maed of alloys. In dialogue with our customers, we
optimise our products to meet the specific application requirements. AILIAI
develops the best alloy material solutions for current and future
challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For
more information on the alloys and services that we supply, call
us at
086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch
on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.