Cu-Mn-Ni-Ag钎料高频感应钎焊2Cr13不锈钢接头的显微组织与性能
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-06-03
采用新型的Cu-Mn-Ni-Ag中温铜基钎料高频感应钎焊2Cr13不锈钢，并对钎料的工艺特性、钎焊接头的显微组织以及测试温度对钎焊接头力学性能的影响进行研究。
Cu-Mn-Ni-Ag钎料高频感应钎焊2Cr13不锈钢接头的显微组织与性能Microstructure and performance of 2Cr13 stainless steel joint by high frequency induction brazing using Cu-Mn-Ni-Ag filler alloy采用新型的Cu-Mn-Ni-Ag中温铜基钎料高频感应钎焊2Cr13不锈钢，并对钎料的工艺特性、钎焊接头的显微组织以及测试温度对钎焊接头力学性能的影响进行研究。结果表明:Cu-Mn-Ni-Ag钎料的熔点约为880 ℃，由富Ag相、Cu-Mn-Ni固溶体以及少量的Ni-Mn-Si化合物组成;钎料与2Cr13不锈钢产生良好的冶金结合，且钎焊接头组织致密;界面反应区的组织为Fe-Mn-Ni-Cr-Cu固溶体，钎缝区组织由富Ag相、Cu-Mn-Ni固溶体和少量的Ni-Mn-Si化合物组成;钎焊接头断裂于钎缝中间的富Ag相和CuMnNi固溶体上，为以剪切韧窝为主的韧性断裂，室温剪切强度最大可达369 MPa，在400 ℃、500 ℃和600 ℃下接头的剪切强度分别为251 MPa、208 MPa和84 MPa。
The characteristic of Cu-Mn-Ni-Ag filler alloy and the microstructure and mechanical properties of the 2Cr13 stainless steel joint brazed by high frequency induction brazing using Cu-Mn-Ni-Ag filler alloy were studied. The results show that the melting point of the Cu-Mn-Ni-Ag filler alloy is 880 ℃ and it is composed of Ag-rich phase, Cu-Mn-Ni solid solution and a little Ni-Mn-Si compound; a layer of Fe-Mn-Ni-Cr-Cu solid solution forms at the interface between the filler alloy and base metal, and the brazing seam zone is composed of Ag-rich phase, Cu-Mn-Ni solid solution and a little Ni-Mn-Si compound. The brazing joints fails in the inside Cu-Mn-Ni solid solution and Ag-rich phase, and the fracture mode of the joints is mainly ductile dimple fracture, the best shear strength of the brazing joint at room temperature is 369 MPa, the high temperature shear strength of the brazing joints at 400 ℃, 500 ℃ and 600 ℃ are 251 MPa, 208 MPa and 84 MPa, respectively.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI
has been a reliable partner and supplier of sophisticated and high-quality
semi-finished products maed of alloys. In dialogue with our customers, we
optimise our products to meet the specific application requirements. AILIAI
develops the best alloy material solutions for current and future
challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For
more information on the alloys and services that we supply, call
us at
086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch
on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.