采用旋转弯曲和超声疲劳实验分别测试了全等轴和等轴双态组织 Ti-6Al-4V 的高周和超高周疲劳性能, 并用 SEM 观察了疲劳断口特征.
微结构和应力比对Ti-6Al-4V合金高周和超高周疲劳行为的影响EFFECTS OF MICROSTRUCTURE AND STRESS RATIO ON HIGH-CYCLE AND VERY-HIGH-CYCLE FATIGUE BEHAVIOR OF Ti-6Al-4V ALLOY采用旋转弯曲和超声疲劳实验分别测试了全等轴和等轴双态组织 Ti-6Al-4V 的高周和超高周疲劳性能, 并用 SEM 观察了疲劳断口特征. 结果表明: 2 种组织 Ti-6Al-4V 合金的高周和超高周疲劳行为相似, 不同应力比下, 其S-N 曲线均表现出单线形或双线形的形式; 存在滑移机制和解理机制2 种疲劳破坏机制. 随应力比增加, 2种组织Ti-6Al-4V合金的高周和超高周疲劳破坏机制均从滑移机制向解理机制转变. 基于疲劳寿命和疲劳强度模型分析了应力比对 2 种机制之间竞争行为的影响, 模型结果与实验结果趋势吻合.
Titanium alloys have been widely used as superior engineering materials because of their high specific strength, high temperature resistance and high corrosion resistance. In their engineering applications such as used in aircraft engines, titanium alloys may experience even 1010 fatigue cycles. Recently, faceted crack initiation was observed in high-cycle fatigue (HCF) and very-high-cycle fatigue (VHCF) regimes of titanium alloys, which resulted in a sharp decrease in fatigue strength. Therefore, the HCF and VHCF of titanium alloys have both scientific significance and engineering requirement. In this work, the effects of microstructure and stress ratio (R) on HCF and VHCF of a Ti-6Al-4V alloy have been investigated. Fatigue tests were conducted on a rotating-bending fatigue machine and an ultrasonic fatigue machine. All the fatigue fracture surfaces were observed by SEM. The results show that the HCF and VHCF behaviors of the fully-equiaxed and the bimodal Ti-6Al-4V alloy are similar. The observations of fracture surface indicate that two crack initiation mechanisms prevail, i.e. slip mechanism and cleavage mechanism. With the increase of stress ratio, the crack initiation mechanism switches from slip to cleavage. The S-N curves present the single-line type or the bilinear type. For the cases of rotating-bending and ultrasonic axial cycling with R=‒1, ‒0.5 and 0.5, the S-N curves are single-line type corresponding to the slip mechanism or cleavage mechanism. For thecases of R=‒0.1 and 0.1, the S-N curves are bilinear type corresponding to both slip and cleavage mechanisms. A model based on fatigue life and fatigue limit is proposed to describe the competition between the two mechanisms, which is in agreement with the experimental results.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.