700~750 ℃GH2984合金的蠕变变形机制
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-04-02
研究铁镍基高温合金GH2984在700~750 ℃蠕变期间的显微组织演变及其对性能的影响。
700~750 ℃GH2984合金的蠕变变形机制Rupture mechanism of GH2984 crept attemperature between 700-750 ℃研究铁镍基高温合金GH2984在700~750 ℃蠕变期间的显微组织演变及其对性能的影响。结果表明：在(700 ℃，300 MPa)蠕变条件下，合金持久寿命仅160 h，变形过程中晶界处的应力集中并促进裂纹的萌生与扩展是造成合金失效的主要原因。应力降至200 MPa时，晶粒旋转导致晶界处应力集中得到释放，抑制裂纹萌生并进而使合金持久寿命明显增长。然而，随着蠕变温度的增加，晶粒在变形过程中伴随出现动态再结晶。这一现象虽然使得合金持久塑性有所增加，但晶粒加工硬化程度较低造成合金持久寿命明显缩短。
The microstructure evolution and its effect on the properties of GH2984 alloy between 700 and 750 ℃ were investigated. The results show the rupture life is only about 160 h when the alloy was crept at 700℃ and 300MPa. The stress concentration and consequently crack nucleation and propagation are the main reason for failure of the alloy. When the stress decreases, the stress concentration is released by the grain rotation. It inhibits the crack nucleation and thus extends the alloy rupture life obviously. However, accompanied with the grain deformation proceeding, the dynamic recrystallization occurs when the creep temperature increases. This leads to the increases of the alloy creep ductility, but decreases the alloy rupture life because of the lower work hardening extent.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.