拉伸保载对2.25Cr1MoV钢高温低周疲劳行为的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-03-31
利用液压疲劳试验机, 采用轴向应变控制方法在455 ℃下对2.25Cr1MoV钢进行高温低周疲劳试验, 通过在峰值应变拉伸时保载0,60,600 s, 研究了拉伸保载时间对该钢低周疲劳行为的影响, 并用扫描电镜对断口形貌进行了观察。
拉伸保载对2.25Cr1MoV钢高温低周疲劳行为的影响Effect of Tensile Holding on High Temperature Low Cycle Fatigue Behavior of 2.25Cr1MoV Steel利用液压疲劳试验机, 采用轴向应变控制方法在455 ℃下对2.25Cr1MoV钢进行高温低周疲劳试验, 通过在峰值应变拉伸时保载0,60,600 s, 研究了拉伸保载时间对该钢低周疲劳行为的影响, 并用扫描电镜对断口形貌进行了观察。结果表明: 2.25Cr1MoV钢呈明显的循环软化特性, 拉伸保载会明显降低循环应力幅, 但保载时间对循环应力幅的影响不大; 拉伸保载使该钢的疲劳寿命降低, 但保载时间超过60 s后, 疲劳寿命基本不受保载时间的影响; 拉伸保载没有改变试验钢的疲劳断裂模式。
High temperature low cycle fatigue test was carried out on 2.25Cr1MoV steel by using a hydraulic fatigue testing system under strain-controlled mode at 455 ℃. Different tensile hold time (0, 60, 600 s) was imposed at peak strain to study the effect of tensile holding load time on low cycle fatigue behavior of the steel. The fracture morphology of the steel was observed by scanning electron microscopy. The results reveal that the steel showed cyclic softening characteristics. The applied tensile holding load caused the stress amplitude obviously reduced, but the holding load time had little effect on cyclic stress amplitude. The fatigue life of the steel decreased because of tensile holding, but the life changed little when holding time exceeded 60 s.The fracture mode was not changed by the tensile holding load.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英，XING，脸书和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn, XING, Facebook and Twitter.