采用100 kN servo-hydraulic MTS型试验机对挤压态AZ31镁合金进行温度为350 ℃、应变速率为0.3 s-1和不同应变量下的热压缩；利用X射线衍射(XRD)测量不同应变量下的织构，并利用取向分布函数计算其织构类型，分析织构转变；通过电子背散射衍射技术(EBSD)分析孪生的形成情况。同时，计算不同滑移系和孪生的斯密特因子，分析不同滑移系和孪生开启的先后次序。
挤压态AZ31镁合金热变形过程中的孪生和织构演变Twinning and texture evolution in extruded AZ31 magnesium alloy during hot deformation采用100 kN servo-hydraulic MTS型试验机对挤压态AZ31镁合金进行温度为350 ℃、应变速率为0.3 s-1和不同应变量下的热压缩；利用X射线衍射(XRD)测量不同应变量下的织构，并利用取向分布函数计算其织构类型，分析织构转变；通过电子背散射衍射技术(EBSD)分析孪生的形成情况。同时，计算不同滑移系和孪生的斯密特因子，分析不同滑移系和孪生开启的先后次序。结果表明：变形初期，由于拉伸孪生的出现导致 (0001) 和(0001) 织构的形成，并随应变量的增加，发生动态再结晶， [0001]和 [0001]纤维织构完全由(0001) 和(0001) 织构代替；在变形初期，大部分晶粒先产生拉伸孪生，接着发生二阶锥面滑移。
The hot compression test was performed on 100 kN servo-hydraulic MTS test machine at temperature of 350 ℃ and strain rate of 0.3 s-1 under different strains. X-ray diffraction (XRD) was used to measure texture. Then, the texture type under different conditions was also calculated using orientation diffraction function under different conditions, aiming to study the texture transformation. The electron back-scattering diffraction (EBSD) was used to analyze twinning. Schmid factor for different slip systems and twinning were calculated to determine the order of initiation of deformation modes. The results indicate that the extension twinning is observed at the early deformation stage, mainly contributing to the formation of (0001) and (0001) texture. [0001] and [0001] fiber texture are finally replaced by (0001) and (0001) texture as the initiation of dynamic recrystallization. At the beginning of deformation, substantial grains firstly occur extension twinning，followed by 2nd-order pyramidal slip.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.