固溶处理对7B04铝合金组织及性能的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-03-04
利用金相组织观察(OM)、扫描电镜分析(SEM)、透射电镜观察(TEM)以及硬度测试，研究固溶处理对7B04铝合金显微组织及硬度的影响。
固溶处理对7B04铝合金组织及性能的影响Effects of solution treatment on microstructures and properties of 7B04 aluminum alloy利用金相组织观察(OM)、扫描电镜分析(SEM)、透射电镜观察(TEM)以及硬度测试，研究固溶处理对7B04铝合金显微组织及硬度的影响。结果表明：实验合金中的η相(MgZn2)为易溶相，S相(Al2CuMg)为难溶相，含Fe杂质相为不溶相；进行单级固溶处理时，随着固溶温度的升高，实验合金的固溶程度、再结晶程度和再结晶晶粒尺寸增加，当温度超过480℃时，出现过烧现象，力学性能恶化，7B04铝合金淬火敏感性较高；双级固溶可有效抑制合金再结晶、降低合金淬火敏感性，实验条件下较好的双级固溶工艺为(450℃, 0.5h)+(490℃, 0.5h)，抑制合金再结晶效果最佳，经120℃时效24h后，硬度达到最大值，为204HV1。
The influence of solution treatments on the microstructure and hardness of 7B04 aluminum alloy were investigated by means of optical microscopy(OM), scanning election microscopy(SEM), transmission election microscopy(TEM) and hardness test. The results show that there are the soluble phaseη(Mg(Zn,Al,Cu)2), the poorly soluble phaseS(Al2CuMg) and the insoluble impurity Fe phase (Al7Cu2Fe). The degree of solid solution and recrystallization increases with the solution temperature increasing gradually. When the temperature exceeds 480℃, overburning on 7B04 alloy occurs and the properties was weakened, 7B04 alloy has high quench sensitivity. However, double-stage solution can inhibit recrystallization of the alloy and decrease the quench sensitivity effectively. The excellent strengthening effect can be expected at (450℃, 0.5h)+(490℃, 0.5h) among the experiments, by which the recrystallization of the alloy can be restrained mostly and the hardness can reach to 204HV1 after aging at 120℃ for 24h.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.