采用动电位极化曲线、电化学阻抗谱(EIS)、SEM, XPS 等分析手段研究了 800 合金在 300 ℃ NaOH 和乙醇胺(ETA)溶液中的腐蚀行为.
Incoloy800合金在300℃ NaOH和ETA溶液中的腐蚀行为CORROSION BEHAVIOR OF ALLOY 800 IN NaOH AND ETA SOLUTIONS AT 300 ℃
采用动电位极化曲线、电化学阻抗谱(EIS)、SEM, XPS 等分析手段研究了 800 合金在 300 ℃ NaOH 和乙醇胺(ETA)溶液中的腐蚀行为. 结果表明, ETA 的添加降低合金的腐蚀电流密度, 增大了氧化膜的膜层电阻; 无论是否添加 ETA, 800 合金均为双层膜结构; 未添加 ETA 时,合金氧化膜外层富 Ni, ETA 添加后氧化膜外层富 Cr. ETA 的添加提高了氧化膜中 Cr 元素的富集程度, 促进了铬氧化物的形成, 增强了 800 合金氧化膜的保护性.
Many components in secondary side of pressurized water reactors (PWRs) are made of carbon steels and low alloy steels. The corrosion products produced by the flow accelerated corrosion (FAC) of these components can deposite on the surface of steam generator (SG) tubes and decrease the heat transfer efficiency of SG tubes. Moreover, the enrichment of foreign ions (e.g. Cl-and Pb2+) occurs with the sedimentation of corrosion products and causes the local environment degradation, and thus accelerates the failure of SG tubes. In order to decrease the FAC of carbon steels and low alloy steels, pH controllers are often added to adjust the pH value of secondary water. The water chemistry environment of secondary side in PWRs has experienced various treatment techniques, such as phosphate treatment, all volatile treatment (AVT), morpholine (MPH) treatment, ethanolamine (ETA) treatment, and boric acid treatment. In comparision with AVT, ETA can significantly reduce the concentration of Fe in the steam-water phase region and water supply system because of its higher alkalinity and lower molar concentration in feedwater. Due to the high resistance to corrosion and stress corrosion cracking in high temperature high pressure water, alloy 800 is often used as steam generator tubes in nuclear power plants and thus becomes ineasingly attractive among researchers. However, few studies focus on the effect of ETA on the corrosion behavior of alloy 800 in high temperature and high pressure water. This work mainly aims to investigate the corrosion behavior of alloy 800 in NaOH and ETA solutions at 300 ℃ by potentiodynamic polarization curve, electrochemical impedance spectra (EIS), SEM and XPS. The electrochemical results demonstrate that the addition of ETA decreases the current density of anodic and cathodic reactions, and increases the corrosion potential of alloy 800. Besides, ETA addition significantly increases the resistance of inner oxide layer and makes the oxide film more compact, which increases the film resistance of alloy 800 in high temperature water. Through the morphology observation and composition analysis, it is found that ETA addition can promote the formation of Cr-rich layer and increase the ratio of chromium in the oxide films although the deposition of magnetite is enhanced on the surface of alloy 800. For stainless steels and nickel-based alloys in high temperature water, the Cr-rich oxide layer can inhibit the diffusion process of O and metal ions, and reduces the corrosion rates of alloys. Therefore, the corrosion resistance of alloy 800 is enhanced after ETA is added in high temperature water.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.