对TC18钛合金直耳片的疲劳性能进行研究，测试在不同处理状态及平均应力水平下耳片的疲劳Smax—N曲线，并利用扫描电镜(SEM)对疲劳试样断口的典型裂纹源形貌和裂纹扩展形貌进行观察分析。
TC18钛合金耳片的断口形貌及疲劳性能Fractograph and fatigue behavior of TC18 titanium alloy lugs对TC18钛合金直耳片的疲劳性能进行研究，测试在不同处理状态及平均应力水平下耳片的疲劳Smax—N曲线，并利用扫描电镜(SEM)对疲劳试样断口的典型裂纹源形貌和裂纹扩展形貌进行观察分析。结果表明：热处理状态和平均应力对耳片疲劳寿命有较大影响；在相同的平均应力下，机械加工后退火处理的试样具有较高的疲劳寿命；在相同退火处理状态下，平均应力水平高，疲劳寿命长；疲劳裂纹主要在夹杂物、材料表面缺陷及次表面内部缺陷等处形成；在裂纹扩展区，对试样加载的应力水平越高，裂纹扩展速率也越大。
The fatigue behavior of straight lugs of TC18 titanium alloy is studied. The fatigue Smax—N curves are tested at different heat treatment status and average stresses. The typical fatigue fracture surfaces are observed and analyzed by SEM (scanning electron microscope). The results show that the heat treatment status and the average stress have obvious influence on the fatigue limit; the fatigue limit of the samples, annealed after machining, is upper at the same average stress; the fatigue limit will be longer when the average stresses are higher at the same annealed status; the fatigue crack mainly initiates at inclusion, surface defect or inner defect on sub-surface; the crack propagation rate will be larger when the load stress is higher in the crack propagation region.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.