Ti-75穿孔管坯的冷扩成形
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-27
研究采用斜轧穿孔及冷扩成形方法制备直径大于130 mm的大口径Ti-75无缝管材的可行性。分别测试穿孔管坯和冷扩后管材的金相组织、力学性能及沿管材轴向方向的裂纹情况。
Ti-75穿孔管坯的冷扩成形Cold expansion forming of Ti-75 perforated tube研究采用斜轧穿孔及冷扩成形方法制备直径大于130 mm的大口径Ti-75无缝管材的可行性。分别测试穿孔管坯和冷扩后管材的金相组织、力学性能及沿管材轴向方向的裂纹情况。结果表明：采用斜轧穿孔方式可以制备Ti-75合金大口径无缝管材且拥有较好的塑性；在室温下，进行冷扩，在扩径率小于15%时，可得到抗拉强度为780 MPa，屈服强度为685 MPa，伸长率为13.5%，断面收缩率为55%的管坯，且不出现扩裂等情况。
The feasibility of preparation of large-diameter seamless pipe of Ti-75 alloy using rotary piercing and cold expansion method. The microstructure, mechanical properties and crack along the pipe axial direction of the situation of the piercing tube and cold-expanded pipe were tested. The results show that Ti-75 large diameter alloy seamless pipe can be prepared using the rotary piercing method and it has a good plasticity. At room temperature, when the expansion of diameter is less than 15%, the tube with tensile strength of 780 MPa, yield strength of 685 MPa, elongation percentage of 13.5% and contraction of area of 55% can be obtained by cold expansion forming. There is no extending cleft in the tube.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.