TC18钛合金棒材组织与探伤的关系
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-26
通过对不同锻造和热处理工艺方案得到的d100 mm TC18钛合金棒材组织和探伤结果进行研究，找出不同工艺方案得到的显微组织所对应探伤水平的变化规律。
TC18钛合金棒材组织与探伤的关系Relationship between microstructure and inspection for TC18 titanium alloy bar通过对不同锻造和热处理工艺方案得到的d100 mm TC18钛合金棒材组织和探伤结果进行研究，找出不同工艺方案得到的显微组织所对应探伤水平的变化规律。结果表明：不同工艺方案得到的典型组织，对应探伤结果存在较大差异；特别是在组织类型均为α+β两相区加工组织的情况下，随着显微组织形貌和大小的变化，探伤杂波水平发生明显变化。
By studying the microstructures and inspection results of d100 mm TC18 titanium alloy bar produced by different forging and heat treatment process, the variation rule of ultrasonic level corresponding to microstructures obtained by different process scheme was found. The results show that the typical microstructures obtained by different process schemes have a great effect on inspection results. Especially the microstructure type is two phase α+β region processing structure. With the variation of the microstructure morphologies and size, the ultrasonic clutter level is changed significantly.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.