氮气气氛下激光切割对TC11钛合金组织及焊接接头性能的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-26
对TC11钛合金在氮气氛下进行激光切割，并在氮气氛下进行热处理，对比热处理前后的显微组织和硬度，确定热影响层深度。去除激光切割影响层后进行电子束焊接，比较研究未激光切割和激光切割焊接接头的拉伸和疲劳性能。
氮气气氛下激光切割对TC11钛合金组织及焊接接头性能的影响Effect of laser cutting in nitrogen atmosphere on microstructure of TC11 titanium alloy and properties of welding joints对TC11钛合金在氮气氛下进行激光切割，并在氮气氛下进行热处理，对比热处理前后的显微组织和硬度，确定热影响层深度。去除激光切割影响层后进行电子束焊接，比较研究未激光切割和激光切割焊接接头的拉伸和疲劳性能。结果表明：激光切割热影响层深度在2~3 mm之间；未激光切割和激光切割TC11钛合金焊接接头低周疲劳性能未见明显差异，但是激光切割后的焊接接头抗拉强度和伸长率相对未激光切割焊接接头分别低45 MPa和3%左右。
TC11 titanium alloy plates were cut by laser and then heat treated in nitrogen atmosphere. The microstructure and microhardness of the surface layers affected by laser cutting were investigated before and after heat treatment. The depth of the heat influence zones by laser cutting was tested. The influenced layers by laser cutting were removed and then the plates were joined by electron beam welding. The effect of laser cutting on the tensile and fatigue properties of the welding joints of TC11 titanium alloy was studied. The results show that the depth of the heat influence zones by laser cutting is in the range of 2 mm to 3 mm. The effect of laser cutting on the low-cycle fatigue property of the welding joint of TC11 titanium alloy is slight, but laser cutting make the tensile strength and elongation percentage decrease by 45 MPa and 3%, respectively.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.