Ti-1023合金d 350 mm棒材的锻造工艺
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-23
通过2种方案试制d350 mm Ti-1023合金棒材，分析2种方案生产的棒材横、纵向组织，力学性能和探伤结果的差异。研究结果表明：铸锭开坯及中间锻造采用1次“高低高”锻造，成品锻造在相变温度以下35~50 ℃进行，变形量大于60%；在该锻造工艺下，可生产出满足X/BS5116标准要求的棒材，且棒材的组织均匀性好。
Ti-1023合金d 350 mm棒材的锻造工艺Forging process of d 350 mm bars of Ti-1023 alloy通过2种方案试制d350 mm Ti-1023合金棒材，分析2种方案生产的棒材横、纵向组织，力学性能和探伤结果的差异。研究结果表明：铸锭开坯及中间锻造采用1次“高低高”锻造，成品锻造在相变温度以下35~50 ℃进行，变形量大于60%；在该锻造工艺下，可生产出满足X/BS5116标准要求的棒材，且棒材的组织均匀性好。
The d350 mm bars of Ti-1023 were manufactured by two solutions, the discrepancies of the microstructures in transverse and longitudinal, the mechanical properties and ultrasonic test results of two bars were analyzed. The results show that in the forging processes, i.e., the breakdown of ingot and intermediate forging adopt “high-low-high” at a time, and the forging of finished products is performed at 35−50 ℃ below the transition temperature and the distortion is greater than 60%. The bars produced can meet the mechanical properties in X/BS 5116 with good homogeneity of structure.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.