研究了TA15钛合金变形量大的d20 mm小棒材及变形量小的大锻件的热处理行为。结果表明：在750~920 ℃范围内，随着退火温度的升高，大锻件拉伸强度升高约100 MPa，小棒材拉伸强度先降后升，且升幅远小于大锻件的；920 ℃以上退火，二者强度都出现降低。随着退火温度的升高，小棒材中再结晶软化率先发挥作用，使拉伸强度降低；而830 ℃以上退火，β转变组织中次生α二次析出起到强化作用，二者抗拉强度均出现升高，但小棒材由于再结晶温度低，再结晶软化削弱了析出强化的作用。
不同变形量TA15钛合金的热处理行为Heat treatment behavior of TA15 titanium alloy with different deformation degrees研究了TA15钛合金变形量大的d20 mm小棒材及变形量小的大锻件的热处理行为。结果表明：在750~920 ℃范围内，随着退火温度的升高，大锻件拉伸强度升高约100 MPa，小棒材拉伸强度先降后升，且升幅远小于大锻件的；920 ℃以上退火，二者强度都出现降低。随着退火温度的升高，小棒材中再结晶软化率先发挥作用，使拉伸强度降低；而830 ℃以上退火，β转变组织中次生α二次析出起到强化作用，二者抗拉强度均出现升高，但小棒材由于再结晶温度低，再结晶软化削弱了析出强化的作用。
The heat treatment behavior of TA15 titanium alloys with different deformation degrees was studied with d20 mm bar and large forging as the representatives for large deformation and small deformation, respectively. The results show that tensile strength increment can be obtained to be 100 MPa for large forging. The tensile strength decreases and then increases for the bar, and the increment is far less than that of large forging when annealed at 750−920 ℃. Both tensile strengths decrease when annealed at temperature higher than 920 ℃. The decrease of the tensile strength for the bar is caused by the recrystallization softening effect with increasing the annealing temperature. The strengthening effect for the little bar and large forging is caused by the secondary phase precipitation from the transformed β above 830 ℃. The precipitation strengthening effect on the little bar is smaller than that of the large forging because of the recrystallization softening effect.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.