热处理对TG6合金热模锻件组织不均匀性的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-19
采用坯料加热温度超过β相变点而模具温度低于β相变点的热模锻造方式，利用光学显微镜和图像分析软件研究双重和三重热处理制度对TG6合金锻件显微组织的影响。
热处理对TG6合金热模锻件组织不均匀性的影响Effects of heat treatment on microstructural inhomogeneity of TG6 alloy hot die forgings采用坯料加热温度超过β相变点而模具温度低于β相变点的热模锻造方式，利用光学显微镜和图像分析软件研究双重和三重热处理制度对TG6合金锻件显微组织的影响。结果表明：TG6合金热模锻件显微组织的不均匀性是由于变形时发生的β→α相变和微区变形的不均匀造成的。热处理制度不能彻底消除TG6合金锻件的显微组织不均匀性，但随高温保温时间的延长，不均匀程度降低。双重热处理时，第一重热处理后的冷却速率越慢，次生α相厚度越大。三重热处理时，第二重较高温度处理可显著地减小次生α相的尺寸。
TG6 alloy was forged by the hot die forging process in which the temperature of the billets was above the β transformation temperature and that of the die was below the β transformation temperature. The effects of double and triplex heat treatments on the microstructures of TG6 alloy forgings were studied by optical microscopy and image analysis software. The results show that the microstructure inhomogeneity is caused by the β→α transformation and the inhomogeneity of microdeforming. The microstructural inhomogeneity does not disappear absolutely after heat treatments, but with the increase of heating time, the inhomogeneity decreases. The thickness of secondary α phase becomes large with decrease of cooling rate after the first heat treatment during the double heat treatment. The second high temperature heat treatment decreases the size of secondary α phase during the triplex heat treatments.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.