固溶处理对近β锻TC21合金组织的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-18
通过对TC21合金进行近β锻，获得典型的双态组织。通过X射线衍射(XRD)、光学显微镜(OM)和扫描电镜(SEM)分析了固溶处理对双态TC21合金组织的影响。
固溶处理对近β锻TC21合金组织的影响Effect of solution treatment on morphology of near β forged TC21 alloy通过对TC21合金进行近β锻，获得典型的双态组织。通过X射线衍射(XRD)、光学显微镜(OM)和扫描电镜(SEM)分析了固溶处理对双态TC21合金组织的影响。XRD分析表明：随着固溶温度的降低，TC21合金固溶水冷处理后的亚稳定相组成依次为α″(≥Tβ)、α+α″(Tβ≈935 ℃)、α+α″+β(915、855 ℃)、α+β(≤835 ℃)。分别对TC21合金进行895 ℃, 2 h，AC、QFC(慢炉冷)、FC+(610 ℃, 4 h，AC)热处理，研究固溶冷却速率对合金组织性能的影响。结果表明：随着冷却速率的增加，等轴α相基本保持不变，次生α相含量减少，合金强度增加，塑性减小。此外，分别对TC21合金在915、905、895、870和835 ℃进行2 h, AC固溶处理，金相分析表明：随着固溶温度的降低，等轴α相相含量及尺寸基本保持不变，次生α条所占比例增加，α条变宽。
Two-state microstructure of TC21 alloy was obtained by near β forging process. The effect of different solution treatments on the microstructure of TC21 alloy was analyzed by X-ray diffractometry (XRD), optical microscopy (OM) and electron microscopy (SEM). The XRD analysis reveals that with the decrease of solution treatment temperature, the phase compositions of TC21 alloy are α″ (≥Tβ), α+α″(Tβ≈935 ℃), α+α″+β (915, 855 ℃), α+β (≤835 ℃). The morphology and mechanical properties of TC21 alloy solution treated at 895 ℃ for 2 h with different solution cooling rate (air cooling, quick furnace cooling, furnace cooling) and then aged by 610 ℃, 4 h, AC was analyzed. As a result, with the increase of solution cooling rate, there is no obvious change on the primary equiaxed α phase, the content of secondary α phase decreases, the strength of the alloy increases, and the plasticity decreases at the same time. TC21 alloy was solution treated at 915, 905, 895, 870 and 835 ℃ for 2 h followed by air cooling, respectively. With the decrease of solution treatment temperature, the width and content of lamellar α phase increase, and there is no difference between the equiaxed α phase of TC21 alloy solution treated at different temperatures.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信，领英和推特与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin, LinkedIn and Twitter.