冷镦和热镦对TC16合金组织和性能的影响
发布人：上海艾荔艾合金股份有限公司www.shailiai.cn
更新时间：2016-01-06
采用Gleeble−3800热模拟机对TC16钛合金丝材分别进行冷镦、热镦实验，利用SEM、TEM、显微硬度计等手段对冷镦、热镦样品及成形后再固溶时效热处理的样品进行显微组织观察和硬度测试。结果表明：冷镦与热镦样品在显微组织和性能上存在差异，但重新固溶时效热处理后，冷镦与热镦样品的显微组织和力学性能接近。
冷镦和热镦对TC16合金组织和性能的影响Effects of cold and hot upset on microstructures and properties of TC16 titanium alloy
采用Gleeble−3800热模拟机对TC16钛合金丝材分别进行冷镦、热镦实验，利用SEM、TEM、显微硬度计等手段对冷镦、热镦样品及成形后再固溶时效热处理的样品进行显微组织观察和硬度测试。结果表明：冷镦与热镦样品在显微组织和性能上存在差异，但重新固溶时效热处理后，冷镦与热镦样品的显微组织和力学性能接近。
The effects of cold and hot upset on the microstructures and properties of TC16 titanium alloy were studied. Means of SEM , TEM and micro-hardness tester were used to analyze the microstructures and hardness of cold and hot upset samples as well as the deformed samples after solution plus aging heat treatment. The results show that although there are some differences between the cold and hot upset samples, their microstructures and properties are nearly the same after solution plus aging heat treatment.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信和领英与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin and LinkedIn.