半固态与铸态7A04铝合金腐蚀行为的对比
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-31
利用金相显微镜分析7A04铝合金半固态与铸态组织，对半固态与铸态7A04铝合金进行极化曲线与阻抗谱电化学测试分析，通过中性盐雾实验对比分析二者的质量损失率、腐蚀面积率和腐蚀坑深度，并采用激光共聚焦显微镜分析腐蚀形貌差异。
半固态与铸态7A04铝合金腐蚀行为的对比Comparison of corrosion behaviors of semi-solid and as-cast 7A04 aluminum alloy
利用金相显微镜分析7A04铝合金半固态与铸态组织，对半固态与铸态7A04铝合金进行极化曲线与阻抗谱电化学测试分析，通过中性盐雾实验对比分析二者的质量损失率、腐蚀面积率和腐蚀坑深度，并采用激光共聚焦显微镜分析腐蚀形貌差异。结果表明：半固态初生α(Al)晶粒细小圆整，半固态试样的耐腐蚀性能优于铸态试样的，半固态试样腐蚀质量损失率较低，半固态试样的蚀坑平均深度及最大深度均小于铸态试样的。半固态工艺可显著提高7A04铝合金的耐腐蚀性能。
The microstructure of semi-solid and as-cast 7A04 aluminum alloys was studied by optical microscopy, and the electrochemical corrosion behavior was investigated mainly by polarization curve and impedance spectroscopy. The mass loss rate, corrosion area rate and corrosion depth were researched by the salt spray corrosion, the corrosion morphologies were observed by laser scanning confocal microscopy. The results show that the semi-solid processing leads to a structure with fine and round grains (primary α(Al)), corrosion resistance of semi-solid sample is better than that of the as-cast sample. Both mass-loss and average corrosion depth of semi-solid sample are smaller than those of the as-cast sample. The semi-solid processing can improve the corrosion resistance of 7A04 aluminum alloy obviously.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博，微信和领英与我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo, Weixin and LinkedIn.