合金成分和冷却速率对Al-Cu合金凝固过程中初生Al2Cu相生长形貌的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-30
针对Al-Cu合金进行研究，研究合金成分、冷却速率等对合金凝固组织及Al2Cu相生长行为的影响，研究结果对Al-Cu系合金开发、组织及性能控制提供参考。
合金成分和冷却速率对Al-Cu合金凝固过程中初生Al2Cu相生长形貌的影响EFFECT OF ALLOY COMPOSITION AND COOLING RATE ON THE PRIMARY Al2Cu PHASE GROWTH MORPHOLOGY OF Al - Cu ALLOY DURING SOLIDIFICATION
对 Al-xCu(x=30,40,45,50,质量分数,%)合金凝固组织进行了系统的观察。结果表明，随合金中Cu含量由30%（质量分数，下同）增加到50%，合金中初生Al2Cu相形貌由枝晶状逐渐转变为棱面状，表明Al2Cu相的生长方式由非小平面生长转变为小平面生长。冷却速率对初生Al2Cu相生长形貌具有重要影响，冷却速率较低时，初生 Al2Cu 相为规则的棱面状；随着冷却速率增大，初生 Al2Cu 相逐渐转变为不规则的非棱面状，表明 Al2Cu 相的生长方式由小平面生长转变为非小平面生长。对凝固过程中初生 Al2Cu相形貌转变研究发现，Cu含量为45%时，初生 Al2Cu 相形貌由枝晶状向方形转变；Cu 含量增加到 50%时，初生 Al2Cu相形貌由枝晶状转变为网状。
Intermetallic compounds have unique natures. Due to the natures of high temperature resistance, high strength and high hardness, intermetallic compounds always exist as strengthening phase in many alloys. The primary Al2Cu phase in Al-Cu alloys is an intermetallic phase. The morphology, size, and distribution of intermetallic compounds phases have largely effects on the mechanical properties of materials.Morphological evolution of intermetallic compoundswas necessarily theoretical basis for intermetallic compound materials for the active control of size, morphology and improving the performance of intermetallic compound materials in the solidification process.At present, there are many reports on the research of Al-Cu alloys. The main research is focused on the eutectic point and 4.7%Cu (atomic percentage)of Al-Cu alloys, but other composition alloys are less considered. The growth mechanism of Al2Cu phase and the primary Al2Cu phase structure of Al-Cu alloy are studied recently. However, the specific growth mechanism of Al2Cu phase is currently not very clear. Alloy composition and cooling rate are often encountered in the ordinary metal melting and solidification. The change of solidification conditions will lead to the transformation of heat and solute in the melt, which will formdifferent morphologies.In this paper, the effect of alloy composition and cooling rateon morphologies and growth behavior of Al2Cu phase in Al-Cu alloyswas studied. Through the microstructure observation of Al-xCu(x=30,40,45,50,quality percentage,similarly hereinafter) alloys, it was found that primary Al2Cu phase morphologies transformed fromdendritic shape to regular bulk with the Cucontentincreased from 30% to 50% in the alloy, which indicated that Al2Cu phase growth changed from non-faceted growth to faceted growth. Cooling rate also had a vital influence on primary Al2Cu phase morphologies. Under low cooling rate, primary Al2Cu phase morphologieswere regular bulk.Themorphologies of primaryAl2Cu phases weretransformed into dendritic shapewith the increasing of cooling rate. Thespecific morphology transformation rule of primary Al2Cu phases in Al-Cu alloys was also studied in the solidification process. It was found that when Cu content was 45%, the morphology transformation of primary Al2Cu phases was from dendritic shape to squaremorphologies. While when Cu content was increased to 50%,the morphology transformation ofprimary Al2Cu phaseswas from dendritic shape to reticular morphologies.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博和微信和我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo and Weixin.