基于末端淬火试验2124铝合金的淬透性
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-26
通过Jominy末端淬火实验研究2124铝合金的淬透性。利用温度数据采集、布氏硬度检测、差示量热法（DSC）和透射电子显微镜（TEM）等手段分析淬火冷却速率对时效后第二相析出行为的影响。
基于末端淬火试验2124铝合金的淬透性Hardenability of 2124 aluminum alloy based on Jominy end quench test
通过Jominy末端淬火实验研究2124铝合金的淬透性。利用温度数据采集、布氏硬度检测、差示量热法（DSC）和透射电子显微镜（TEM）等手段分析淬火冷却速率对时效后第二相析出行为的影响。结果表明：Jominy末端淬火2124铝合金室温水淬硬度下降小于10%的淬透深度大约为50 mm，该位置处合金在222.7~350.0 ℃温度区间的平均淬火冷却速率大于2.0 ℃/s；较低的淬火冷却速率致使过饱和的溶质原子和空位损失，导致时效析出相变驱动力不足，显著削弱了时效强化效果。
The hardenability of 2124 aluminum alloy was investigated by means of Jominy end quench test. The effects of cooling rate on ageing precipitation and strengthening behavior were analyzed by temperature data acquisition, Brinell hardness measurement, differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) observation. The results show that the hardening depth with hardness loss below 10% of 2124 alloy Jominy specimen quenched by room temperature water is approximately 50mm where the average cooling rate through the temperature range from 222.7 ℃ to 350.0 ℃ is above 2.0 ℃/s. The age hardening response of 2124 alloy is obviously weakened at slower quenching rate, which is caused by the loss of vacancies and solutes.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博和微信和我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo and Weixin.