Mg和Zn对2099合金时效组织与拉伸性能的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-24
通过常规力学性能测试和透射电镜微观组织观察，研究2099合金在不同热处理状态(T6和T8)下的微观组织和拉伸性能，以及2099合金中所含少量Mg和Zn对合金组织与性能的影响。
Mg和Zn对2099合金时效组织与拉伸性能的影响Effect of Mg and Zn on microstructure and tensile properties of 2099 alloy
通过常规力学性能测试和透射电镜微观组织观察，研究2099合金在不同热处理状态(T6和T8)下的微观组织和拉伸性能，以及2099合金中所含少量Mg和Zn对合金组织与性能的影响。结果表明：2099合金在T6峰时效条件下，主要强化相是δ′相、θ′相和T1相；在T8峰时效下，主要强化相是δ′相、T1相和少量θ′相，预拉伸变形促进T1相的析出，提高合金的时效强化效果；Mg的添加促进GP区和θ′相的析出，Zn的添加有利于T1相生成和弥散分布；而Mg和Zn同时添加显著地促进T1相析出，并抑制δ′相的粗化。
The tensile properties and microstructure of 2099 alloy in T6 and T8 tempers were investigated by tensile test and TEM observation. Moreover, the effects of the Mg and Zn in 2099 alloy on the microstructure and properties of alloy were studied. The results show that under T6 peak aged condition, the dominant precipitates are δ′, θ′ and T1 phases. While under T8 peak aged condition, the major precipitates contain δ′ phase, T1 phase and θ′ phase with small volume fractions. The pre-stretching prior to ageing promotes the precipitation of T1 phase, thus improves ageing strengthening. Mg addition promotes the precipitation of GP zone and θ′ phase while Zn facilitates T1 phase precipitation. The addition of Mg together with Zn stimulates the formation of T1 phase obviously, and suppresses the coarsening progress of δ′ phase.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博和微信和我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo and Weixin.
前一页：不锈钢丝加工常见的误区
后一页：纵向磁场作用下DZ417G高温合金的枝晶生长行为