TA15钛合金薄壁焊接件热处理校形研究
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-18
针对飞机关键薄壁件焊接过程中产生的“簸箕”变形问题，采用有限元结合实验验证的方法进行了焊接变形及焊后热处理校形的研究。通过实验获得了材料的基础物性及高温蠕变行为，验证了焊接及焊后热处理有限元模型。利用可靠的热处理有限元模型进行了热处理工艺优化。
TA15钛合金薄壁焊接件热处理校形研究STUDY ON SHAPE CORRECTION OF THE THIN PLATE OF TA15 TITANIUM ALLOY BY POST WELD HEAT TREATMENT
针对飞机关键薄壁件焊接过程中产生的“簸箕”变形问题，采用有限元结合实验验证的方法进行了焊接变形及焊后热处理校形的研究。通过实验获得了材料的基础物性及高温蠕变行为，验证了焊接及焊后热处理有限元模型。利用可靠的热处理有限元模型进行了热处理工艺优化。结果表明，筋条焊后开槽导致沿筋条方向的应力释放及筋条-长衍焊点是导致“簸箕”变形的主要原因；提高温度、增加载荷及延长保温时间能够改善热处理校形的效果，并据此制定了面向工程应用的TA15 钛合金薄壁构件的热处理工艺图。
Weld deformation of the thin-wall weldment used in fighter aircraft not only hinders its subsequent procedure of fabrication and assembling, but also reduces its fatigue strength. As a result, weld deformation shortens its service lifeessentially. Dustpan deformation is always produced in the thin-wall weldment after multiple-pass weld. In this paper, combining with the experiment, the finite element method was adopted to analysis the deformationof the thin-wall weldment by multiple-pass weld and its shape correction by post weld heat treatment. For obtaining the fundamental properties such as thermal parameters and mechanical parameters of TA15 titanium alloy, a series of experiments were conducted at room temperature and high temperatures. Additionally, creep behaviors of TA15 titanium alloy were studied at the temperatures of 500℃, 550℃, 600℃, 650℃, 700℃ and 750℃, and the parameters of creep constitutive equations of the alloy were obtained with considering the analysis of post weld heat treatment. A thermal coupled temperature – displacement analysis for welding and post weld heat treatment was performed on a three dimentional shell model of protective gille. Experiments of multiple-pass weld and post weld heat treatment were used to testify the reliability of the finite element model of welding and post weld heat treatment. With using the reliable finite element model, the parameters of heat treatment were studied. The study indicates that: the fabrication on the crossing of structure section and fillet after fillet - wallboard weld leads the compression deformation release along the fillet, after that, the shrinkage distortion produced during spot welding of fillet - structural section mainly contributes the large dustpan deformation of the thin-wall weldment; increasing temperatures, enlarging loads and prolonging the hold time can improve the shape correction of the thin-wall weldment during post weld heat treatment, hence we worked out the guide maps of the post weld heat treatment for shape correction of the thin-wall weldment under 700℃ and 750℃.
作为值得信赖的合作伙伴和高品质金属合金的半成品供应商，艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中，我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求，艾荔艾致力于为客户提供最佳的金属材料解决方案。
AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博和微信和我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo and Weixin.