渗注磷酸盐对AZ31镁合金疲劳裂纹扩展的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-12-08
交变载荷作用下在AZ31镁合金疲劳裂纹尖端渗注磷酸盐转化液，研究磷酸盐的沉积行为及其对AZ31镁合金疲劳裂纹扩展速率的影响。采用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)观察分析裂纹尖端的形貌和物相组成，并采用贴应变片方法确定渗注磷酸盐转化液前后应力强度因子的变化。
渗注磷酸盐对AZ31镁合金疲劳裂纹扩展的影响Effects of immersing phosphate on fatigue crack propagation in AZ31 magnesium alloy
交变载荷作用下在AZ31镁合金疲劳裂纹尖端渗注磷酸盐转化液，研究磷酸盐的沉积行为及其对AZ31镁合金疲劳裂纹扩展速率的影响。采用扫描电镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)观察分析裂纹尖端的形貌和物相组成，并采用贴应变片方法确定渗注磷酸盐转化液前后应力强度因子的变化。结果表明：渗注的磷酸盐转化液在AZ31镁合金疲劳裂纹尖端形成Zn3(PO4)∙4H2O及MgZnP2O7复合覆层，能改变疲劳裂纹尖端的应力大小和分布状态，使应力强度因子降低约30%，从而有效地增强疲劳裂纹闭合效应，降低或延滞AZ31镁合金疲劳裂纹的扩展。
Under alternate loads, a phosphate liquid was immersed into the fatigue crack tip of AZ31 magnesium alloy, the phosphate deposition behavior and effects of the phosphate film on the fatigue crack propagation rate at the fatigue crack tip of AZ31 magnesium alloy were investigated. The morphologies and phase constitutions of the phosphate deposition at the fatigue crack tip were characterized by scanning electron microscopy (SEM), energy spectrum analysis (EDS) and X-ray diffractometry (XRD), respectively. The stress-intensity factor values at the fatigue crack tip were compared with and without inmersing phosphate liquid by taking advantage of strain gauge. The results show that the phosphate( Zn3(PO4)∙4H2O and MgZnP2O7) films can be formed at the fatigue crack tip of AZ31 alloy through inmersing phosphate liquid, and the stress magnitude and distribution change after inmersing phosphate liquid at the fatigue crack tip of AZ31 alloy. The stress-intensity factor value decreases by about 30%, which effectively improves the fatigue crack closure, and reduces or arrearage the fatigue crack propagation.
获取更多我们供应的合金和服务信息，请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们，您也可以通过微博和微信和我们互动。
For more information on the alloys and services that we supply, call us at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on Weibo and Weixin.