双级时效对1973铝合金组织和性能的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-11-03
采用透射电镜观察、硬度和电导率测试等手段研究双级时效对1973高强高韧铝合金组织和性能的影响。
双级时效对1973铝合金组织和性能的影响Effect of two-stage ageing on microstructures and properties of 1973 aluminum alloy
采用透射电镜观察、硬度和电导率测试等手段研究双级时效对1973高强高韧铝合金组织和性能的影响。结果表明：一级时效温度对合金最终组织和性能的影响不大，二级时效温度和时间对1973铝合金硬度和电导率的影响明显；1973铝合金适宜的双级时效工艺为(120 ℃, 6 h)＋(160 ℃, 16 h)，在此条件下，合金的硬度和电导率分别为191HV和38.0%(IACS)，其显微组织特点为晶内沉淀相呈细小弥散状分布，而合金的晶界沉淀相粗大、呈断续状分布，并且有较明显的无沉淀析出带。合金中主要沉淀相为η'相和η相，此外还有少量的GPⅡ区。
The two-stage ageing on the microstructures and properties of 1973 aluminum alloy were studied by means of transmission electron microscopy (TEM), hardness and conductivity measurements. The results show that the temperature and time of the second-stage ageing have a key effect on the properties of the alloy, while the temperature of the first-stage ageing has little effect on them. The best two-stage ageing process for this alloy is: (120 ℃, 6 h)＋(160 ℃, 16 h). Under this condition, the hardness and electrical conductivity of this alloy are 191HV and 38.0%(IACS), respectively. The microstructure of this alloy is that the nano scale precipitates disperse inside the grain, and the coarse-discontinuous precipitates occur along the grain boundaries. The precipitated-free zones (PFZ) appear on the grain boundaries. The main precipitates are η and η' phases, and with minous GPⅡ zone.
以上资料由上海艾荔艾金属材料有限公司提供，欢迎新老客户来电洽购。
本文来自上海艾荔艾金属材料有限公司http://www.shailiai.com，转载请注明出处。