采用透射电子显微镜(TEM)、选区电子衍射(SADP)和硬度测试等手段研究1973高强高韧铝合金在不同温度下的单级时效析出及硬化行为。
1973高强高韧铝合金的时效析出及硬化行为Ageing precipitation and hardening behavior of 1973 high strength andhigh toughness aluminum alloy
采用透射电子显微镜(TEM)、选区电子衍射(SADP)和硬度测试等手段研究1973高强高韧铝合金在不同温度下的单级时效析出及硬化行为。结果表明：1973铝合金在120和140 ℃有很强的抗过时效能力，峰时效过后，硬度在长时间内基本保持在195 HV附近。1973铝合金的析出序列为：α过饱和固溶体(SSS)→GPⅠ区/GPⅡ区→η'亚稳相→η平衡相→T相。在140 ℃单级时效过程中，GPⅡ区和η'相一直都存在于时效合金中，对合金起着最大的强化作用。
The ageing precipitation and hardening behavior of 1973 high strength and high toughness aluminum alloy were studied by means of transmission electron microscopy (TEM), select area electron diffraction (SAED) and hardness measurements at different ageing temperatures. The results show that this alloy has obvious anti-over-aging capability at 120 and 140 ℃. And this alloy can keep the hardness of 195 HV in a long time after peak-ageing. Furthermore, the precipitation sequence of 1973 aluminum alloy can be described as follows: supersaturated solid solution(α)→ GPⅠ/GPⅡ zone→ metastable η'→ stable η→T phase. There are GPⅡ zone and η' phase with the greatest strengthening effect on the 1973 aluminum alloy during the whole ageing process at 140 ℃.
以上资料由上海艾荔艾金属材料有限公司提供，欢迎新老客户来电洽购。
本文来自上海艾荔艾金属材料有限公司http://www.shailiai.com，转载请注明出处。