针对等离子旋转电极工艺制备的FGH96合金粉末，采用俄歇电子能谱对合金粉末的颗粒表面进行成分分析，并利用透射电镜对预热处理后粉末中的碳化物演变进行研究。
FGH96合金粉末的俄歇分析及预热处理AES analysis and pre-heat treatment of FGH96 superalloy powders
针对等离子旋转电极工艺制备的FGH96合金粉末，采用俄歇电子能谱对合金粉末的颗粒表面进行成分分析，并利用透射电镜对预热处理后粉末中的碳化物演变进行研究。结果表明：FGH96合金粉末的颗粒表面明显存在O、C和Ti元素的偏聚，原始合金粉末的颗粒表面由O和C 原子吸附层和富含Ti元素的碳−氧化物层组成；经过预热处理，颗粒中形成于快速凝固过程中的MC′亚稳碳化物转变成稳定的MC碳化物，并析出M23C6碳化物，明显改善了颗粒内碳化物的稳定性和分布状态。
The chemical composition on particle surface of FGH96 superalloy powders was analyzed by means of auger electron spectroscopy (AES), and the carbide evolution after pre-heat treatment was also analyzed by TEM. The results show that elements O, C and Ti segregate on the particle surface, which is composed of absorption layer and oxy-carbides layer. The absorption layer is mainly composed of O and C atoms, while the oxy-carbides layer is characterized as Ti oxide and carbide. MC′ metastable carbide precipitates during the quick solidification, after the pre-heat treatment, the metastable carbide MC′ changes to stable MC carbide and M23C6 precipitates. This improves the stability and distribution state of carbide in the particles.
以上资料由上海艾荔艾金属材料有限公司提供，欢迎新老客户来电洽购。
本文来自上海艾荔艾金属材料有限公司http://www.shailiai.com，转载请注明出处。
前一页：初生α相含量对TC4 ELI钛合金动态应力−应变行为的影响
后一页：首饰金属材料