人工时效对6005A铝合金晶间腐蚀性能的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-10-17
采用硬度测试、晶间腐蚀试验、金相及透射电镜观察研究人工时效对6005A铝合金晶间腐蚀性能的影响。
人工时效对6005A铝合金晶间腐蚀性能的影响Effect of artificial ageing on intergranular corrosion of 6005A Al alloy
采用硬度测试、晶间腐蚀试验、金相及透射电镜观察研究人工时效对6005A铝合金晶间腐蚀性能的影响。结果表明：6005A铝合金在固溶水淬后进行人工时效，晶间腐蚀敏感性随时效时间的延长而变化；时效初期，合金的晶间腐蚀敏感性很低，随时效时间的延长，晶间腐蚀敏感性增加；时效12 h时，合金硬度达峰值，同时晶间腐蚀敏感性也达最大，随后晶间腐蚀敏感性减弱，出现点蚀。6005A铝合金晶间腐蚀敏感性与晶界有关，点蚀的引入与晶内Q′相的析出长大有关。
The effect of artificial ageing on the corrosion performance of 6005A Al alloy was investigated by hardness test, intergranular corrosion test, optical microscopy and TEM observation. The results show that the intergranular corrosion susceptibility of 6005A Al alloy is related to the artificial ageing time. The accelerated corrosion test reveals that the intergranular corrosion(IGC) of 6005A Al alloy is low susceptible to in the beginning of the artificial ageing after water quenched. However, IGC susceptibility increases with the increase of aging time, and reaches the peak value after artificial ageing for 12 h, while the hardness is the highest. The overageing reduces the IGC susceptibility, however, the slight pitting is produced. The increased IGC susceptibility is related to the grain boundary. The pitting susceptibility by over ageing is evolved due to coarsening of the Q′-phase particles.
以上资料由上海艾荔艾金属材料有限公司提供，欢迎新老客户来电洽购。
本文来自上海艾荔艾金属材料有限公司http://www.shailiai.com，转载请注明出处。