双重退火对BTi-6431S合金板材组织与性能的影响
发布人：上海艾荔艾金属材料有限公司www.shailiai.com
更新时间：2015-09-09
采用光学显微镜、室温和高温拉伸实验研究热处理对BTi-6431S合金板材微观组织和力学性能的影响。
双重退火对BTi-6431S合金板材组织与性能的影响Effect of double annealing on microstructure and mechanical properties of BTi-6431S plate
采用光学显微镜、室温和高温拉伸实验研究热处理对BTi-6431S合金板材微观组织和力学性能的影响。结果表明：升高第一阶段的退火温度，块状初生α相粗化，趋于等轴状，体积分数逐渐降低。β相和次生α相的体积分数增加。室温强度和塑性变化不大。高温强度随第一级退火温度的升高而逐渐上升，塑性下降。在相同第一阶段退火温度下，第二阶段退火温度的升高使得初生α相含量急剧增加，趋于板条状，β转变组织含量降低，室温和高温拉伸性能同时下降。通过合理的控制双重退火的温度，可使BTi-6431S合金具有良好的高温强度和室温塑性的匹配。
The influence of variant heat treatment processing (double annealing) on the microstructure and mechanical properties of the BTi-6431S plate were investigated by optical microscope and tensile tests at room and elevated temperatures. The results show that, with the first stage annealing temperature increasing, the shape of primary α phase (αp) becomes coarse, changes into equiaxial, and its volume fraction decreases gradually, while the volume fractions of β-matrix (βt) and secondary α phase increase. The room temperature strength and ductility have not obvious variation, but the high temperature strength increases and the ductility decreases. However, after the first annealing at the same temperature, increasing secondary aging temperature promotes αp transforming into lath-shape, meanwhile reducing the volume fraction of βt, resulting in the mechanical properties decreasing. The best alloy microstructure with good high temperature strength and room temperature plasticity can be obtained by choosing double annealing temperature parameter reasonably.
以上资料由上海艾荔艾金属材料有限公司提供，欢迎新老客户来电洽购。
本文来自上海艾荔艾金属材料有限公司http://www.shailiai.com，转载请注明出处。