Ti55531合金连续升温过程的相变行为Phase transformation of Ti55531 alloy during continuous heating process

通过连续升温热膨胀法分析Ti55531(Ti-5Mo-5Cr-5V-3Al-1Zr)合金在连续升温过程中的热膨胀行为、物相组成和显微组织，绘制热膨胀微分曲线。结果发现：随着升温速率的增加，相变温度逐渐升高。其中，在1 ℃/min的升温速率下不同温度区间内的相变行为如下：低于192 ℃时，发生ω_ath→β转变；192~347 ℃时，发生β→ω_iso转变；347~376 ℃时，发生ω_iso→α+β、β→α转变；409~648 ℃时，发生β→α转变；648~831 ℃时，发生α→β转变；831 ℃时，转变为全β组织。计算得到α→β转变热激活能为188.04 kJ/mol。

The dilatometry behavior, phase composition and microstructure of Ti55531(Ti-5Mo-5Cr-5V-3Al-1Zr) alloy were investigated during continuous heating process, and the derivative of dilatometric curve was thereby calculated. The results show that the phase transformation temperature increases with accelerating heating rate. Consequently, phase transformation sequence of Ti55531 alloy at heating rate of 1℃/min is confirmed as follows: temperature below 192 ℃, ω_ath transforms β; 192-347 ℃, β transforms ω_iso; 347-376 ℃, ω_iso transforms α+β and β transforms α; 409-648 ℃, β transforms α; 648-831 ℃, α transforms β; over 831 ℃, full β. The activation energy value relating to α→β transformation in Ti55531 alloy is evaluated as 188.04 kJ/mol.

全文下载：http://pan.baidu.com/s/1nt3R7df