(2) 化学成分:暂时不对外公布。

(3) 力学性能
 1) 冲击吸收能量：温度 20°C/300°C/600°C/650°C/700°C, 冲击吸收能 65.5J/101J/235J/294J/294J。
 2) 钢的耐回火性: 回火温度100°C /200°C/300°C/400°C /450°C/500°C/525°C/550°C/575°C/580°C/600°C/620°C /640°C/650°C/675°C/680°C/700°C。硬度52HRC/52HRC/48HRC/46HRC/46HRC/43HRC/45HRC/45HRC/43HRC/43HRC/40HRC/39HRC/37HRC/37HRC/32HRC/

30HRC/28HRC
 3) 热加工性能: 温度 800°C/900°C/1000°C/110o°C/1200°C,抗拉强度162.3MPa /145.9MPa/75.4MPa/41.76MP3/27.09MPa, 伸长率 39.7%/49.6%/ 59.1%/ 74.9%/ 77.7%。
 4) 拉伸性能:温度25°C/300°C/600°C/650°C/700°C, 抗拉强度 1395MPa /1291MPa/886MPa/620MPa/356MPa; 屈服强度 1236MPa/ 1073MPa/ 741MPa/ 520MPa/290MPa; 伸长率17.3%/17.4%/26%/30.3%/42%;断面收缩率 61%/66.4%/84.7%/90.2%/95.1%
(4) 热加工规范:加热温度1150~1180°C, 开始温度1150~1180,终止温度≥930°C

 (5) 淬火、回火规范:淬火温度 900 ~920°C, 在20 ~60°C 的油中冷却到室温, 硬度 42 -44HRC.回火温度 560 ~580°C, 硬度 40~42HRC
(6) 典型应用举例:用于大截面热锻模具、辊锻模具。